Abstract

onic Liquids have emerged as effective lubricants and additives to lubricants, in the last decade. Halogen-free ionic liquids have recently been considered as more environmentally stable than their halogenated counterparts, which tend to form highly toxic and corrosive acids when exposed to moisture. Most of the studies using ionic liquids as lubricants or additives of lubricants have been done experimentally. Due to the complex nature of the lubrication mechanism of these ordered fluids, the development of a theoretical model that predicts the ionic liquid lubrication ability is currently one of the biggest challenges in tribology. In this study, a suitable and existing friction model to describe lubricating ability of ionic liquids in the elastohydrodynamic lubrication regime is identified and compared to experimental results. Two phosphonium-based, halogen-free ionic liquids are studied as additives to a Polyalphaolefin base oil in steel–steel contacts using a ball-on-flat reciprocating tribometer. Experimental conditions (speed, load and roughness) are selected to ensure that operations are carried out in the elastohydrodynamic regime. Wear volume was also calculated for tests at high speed. A good agreement was found between the model and the experimental results when [THTDP][Phos] was used as an additive to the base oil, but some divergence was noticed when [THTDP][DCN] was added, particularly at the highest speed studied. A significant decrease in the steel disks wear volume is observed when 2.5 wt. % of the two ionic liquids were added to the base lubricant.

Publication Date

5-19-2016

Document Type

Article

Department, Program, or Center

Mechanical Engineering (KGCOE)

Campus

RIT – Main Campus

Share

COinS